MOD. | THERMAL INSULATION | REACTION TO FIRE | DIELECTRICAL INSULATION | MATERIAL |
---|
. | . | . | . | . |
PVC Flex | +70°C | — | 25 kV/mm | Plasticized polyvinyl chloride |
PVC-HT / PVC-HT ANTI-OIL | +105°C | UL 1581 | 20 kV/mm | Plasticized polyvinyl chloride |
TERMORESTR. H1 | +105°C | Not Self-Ext. | 600V (0.6 kV) | Cross-linked polyolefin |
T.H.T. | +120°C | Not Self-Ext. | 1500V (1.5 kV) | Rayon-Viscose |
—————————– | —————————– | —————————– | —————————– | —————————– |
TERMORESTR. H2 | + 125°C | V-1 | 600V (0.6 kV) | Cross-linked polyolefin |
TPE TERMOPLASTICA | + 125°C | UL 94 HB | 15 kV/mm | Olefin thermoplastic rubber |
TERMORESTR. H2-MIL | +135°C | V-1 | 600V (0.6 kV) | Cross-linked polyolefin |
HDR / HDR-TW DIESEL | +150°C | SAE-AMS-DTL-23053/16 | Space Factor | Modified irradiated fluoro-elastomer |
T.V.S. | +155°C | Not Self-Ext. | 1500V (1.5 kV) | Glass Fiber and Acrylic Varnish |
G.P.E. V-2 / G.P.E. V-0 | +155°C | V-2 / V-0 | — | Polyester PET braided |
TERMORESTR. KYNAR® | +175°C | V-1 | 30 kV/mm | Polyvinylidene fluoride (PVDF) |
—————————– | —————————– | —————————– | —————————– | —————————– |
TERMORESTR. VITON® | +200°C | V-1 | 15 kV/mm | Fluoroelastomer |
T.V.E. | +200°C | V-1 | 1.5/2.5/4.0 kV IMQ and other | Glass Fiber and Extruded Silicone |
D 19.61 | +200°C | V-1 | 15 kV/mm | Extruded silicone |
—————————– | —————————– | —————————– | —————————– | —————————– |
G.V.H. / Tipo D | +240°C | V-1 | 1000V (1.0 kV) | Glass Fiber and Synthetic Resin |
T.V.E. FIRE SLEEVE | +250°C | V-1 | >1.5 kV | Glass Fiber and Extruded Silicone |
TERMORESTR. HTFE TEFLON | +260°C | V-0 | 40 kV/mm | PTFE |
PTFE “SPAGHETTI” | +300°C | V-0 UL94 | Min. 20 Kv/mm | PTFE |
—————————– | —————————– | —————————– | —————————– | —————————– |
G.V. / G.V. D. | +450°C | V-0 | 800V (0.8 kV) | Glass Fiber |
—————————– | —————————– | —————————– | —————————– | —————————– |
G.F.B. / G.F.B.I. | +600°C | V-0 | 600V (0.6 kV) | Basalt Fiber |
G.F.C. | +650°C | V-1 | — | Carbon PAN Fiber |